STANNOL FLUX GEL MULTIFIX 450-1 10ML
Acid value: 65-75 mg KOH/g
Viscosity: 450-650 Pa*s
Halide content: none
Water content: <0.5%
Density (at 20° C): 0.82 g/cm³
Flashpoint (closed crucible): 93°C
Out of stock
PRODUCT NOT IN STOCK AT THE MOMENT
Send me an email when available
Flux-Gel MultiFix Stannol 450-01
The Flux-Gel Multifix 450-01 has been specially developed for rework and repairs in the electronics industry.
The flux gel is suitable both for manual application as well as for automatic application using a dispenser.
Stannol Multifix 450-01 was specially developed for rework and repair. It is a resin-based, no-clean, tacky flux,
suitable for manual and automatic dispensing, with good printability and fine dispensability.
The extreme low activation causes an excellent insulation reaction of the flux residues after soldering.
Therefore Multifix 450-01 is excellently suitable for many applications in electronics.
The residues of Multifix 450-01 dry quickly, are hard and not sticky.
Characteristics:
The Flux-Gel Multifix 450-01 offers the following advantages:
No Clean
Halide free
Dispensable
Application:
Apply a sufficient quantity of Multifix 450-01 manually or with a compressed air dispenser.
The soldering temperature should not exceed 350°C.
To evaporate the solvent make sure that the flux is heated above 100°C.
This assures a non-sticky film.
Physical Properties And Data:
General Properties Multifix 450-01
Acid value: 65-75 mg KOH/g
Viscosity: 450-650 Pa*s
Halide content: none
Water content: <0.5%
Density (at 20° C): 0.82 g/cm³
Flashpoint (closed crucible): 93°C
Reliability Tests:
Change of surface resistance DIN 8527: pass
Corrosion DIN 8527: pass
Copper mirror test: pass